HDPE is not recommended for purging as it can cause delamination or lead to black specks. Sink Marks Melt too hot • Decrease nozzle and barrel temperatures • Decrease mold temperature Insufficient material volume • Adjust transfer position • Increase shot size • Increase injection rate • Increase packing pressure Part geometry too thick • Reduce wall thickness • Reduce rib thickness TROUBLESHOOTING RECOMMENDATIONS PROBLEM CAUSE SOLUTION Flash Injection pressure too high • Decrease injection pressure • Increase clamp pressure • Decrease injection rate • Increase transfer position Excess material volume • Adjust transfer position • Decrease pack pressure • Decrease shot size • Decrease injection rate Melt and/or mold temperature too hot • Decrease nozzle and barrel temperatures • Decrease mold temperature Loose clamp • Reset mold height • Increase clamp tonnage Shrink Too much shrink • Increase cooling time • Decrease mold temperature Too little shrink • Decrease cooling time • Increase mold temperature Burning Process related • Decrease nozzle and barrel temperatures • Decrease mold temperature • Decrease injection rate • Reduce decompression Mold design • Clean, widen and increase number of vents • Increase gate size to reduce shear Wet material • Verify material is dried at proper condition Nozzle Drool Nozzle temperature too hot • Decrease nozzle temperature • Decrease back pressure • Increase screw decompression • Verify material has been dried at proper conditions Incorrect nozzle • Use reverse taper tip Weld Lines Melt front temperatures are too low • Increase injection rate • Increase pack and hold pressure • Increase melt temperature • Increase mold temperature Mold design • Increase gate size • Identify end of fill pattern and verify proper vent location • Add vents or increase vent width • Move gate location TROUBLESHOOTING RECOMMENDATIONS PROBLEM CAUSE SOLUTION Warp Process related • Increase melt temperature • Reduce injection speed • Increase pack pressure • Increase pack time • Decrease mold temperature • Increase cool time Mold design • Non-uniform mold cooling Part design • Non-uniform wall thickness Thermolator incorrect temperature • Check settings • Inspect thermocouple Sticking in Mold Overfilled cavity • Decrease injection rate and pressure • Decrease hold pressure • Adjust transfer position • Decrease nozzle and barrel temperatures • Decrease mold temperature • Decrease cooling time Part too hot • Decrease barrel temperature • Decrease mold temperature • Increase cooling time Mold design • Increase draft angle • Polish cores in direction of ejection Black Specks Contamination • Purge machine Degradation • Reduce melt temperature • Reduce screw speed • Reduce back pressure Machine related • Check for wear on screw, barrel or check ring Delamination Process related • Increase melt temperature • Decrease injection speed • Purge barrel to eliminate material contamination Mold design • Reduce sharp corners in material flow path • Increase venting TROUBLESHOOTING RECOMMENDATIONS PROBLEM CAUSE SOLUTION Discoloration Oversheared material • Decrease melt temperature • Decrease injection speed • Reduce residence time Mold design • Increase gate sizing Dry material • Check moisture of material to ensure it is within the recommended moisture percentage for molding TROUBLESHOOTING RECOMMENDATIONS 1.844.4AVIENT www.avient.com Copyright © 2021, Avient Corporation.

% Pigment Specific Gravity Color Index Heat Stability Lightfastness System BROWN 83MB01 (c) Iron Oxide, Tan HR 60 1.78 PBr-11 1 I/O SBR 83MB02 (c) Iron Oxide, Light 68 2.1 PBr-6 2 C I/O SBR 83MB03 (c) Iron Oxide, Dark 60 1.83 PBr-6 2 C I/O SBR 83EP02 Iron Oxide, Light 69 1.98 PBr-6 2 C I/O EPDM 83EP03 Iron Oxide, Dark 69 1.98 PBr-6 2 C I/O EPDM BLACK 90MB01 (c) Furnace N-330 31 1.2 PBk-7 1 I/O SBR 90MB05 (c) Iron Oxide 60 1.8 PBk-11 2 C I/O SBR 90EP01 Furnace Black 33 1.05 PBk-7 1 I/O EPDM 90EP05 Iron Oxide 55 1.56 PBk-11 2 C I/O EPDM ALUMINUM 61MB01 Aluminum 70 1.5 PM-1 1 I/O SBR 61EP01 Aluminum 60 1.31 PM-1 1 I/O EPDM RS = Red Shade YS = Yellow Shade VYS = Very Yellow Shade BS = Blue Shade VBS = Very Blue Shade GS = Green Shade NC = Non-Crystallizing HR = Heat-Resistant (a) = Potential Migration at Low Use Levels (b) = Poor Alkali Resistance - Not Recommended for Open Steam Cure (c) = Six Month Shelf Life LIGHTFASTNESS I = Indoor Only I/O = Indoor or Outdoor Mass = Outdoor Masstone Application Only C = Some Caution Advised HEAT STABILITY 1 = Above 400°F 2 = 350°F–400°F 3 = Below 350°F C = Some Caution Advised 1.844.4AVIENT www.avient.com Copyright © 2024, Avient Corporation.

功能 目标应用 血液采集 试剂容器/试剂盒 移液器/ 器具 设备/配件     即用型配方避免对分析测试的干扰； 可萃取金属数据              聚合物对激光能量的激活可提供高 对比度、无溶剂的 高速鉴别     定制母粒和即用型配方可提供 透明和不透明颜色，同时允许激光 传输/吸收    PE和PP的新一代快速成核剂；提 高尺寸稳定性，热性能和机械性能  降低湿蒸汽透过率（MVTR） HDPE即用型配方 吸湿母粒   减少 BCT（血液收集管）中因氧传 输造成的真空损失，并保护试剂免 受氧化降解   在290-450nm波长范围内阻挡紫 外线，对透明度没有影响；保护光 敏试剂     自检/即时检验 （POCT） 用于实验室自动化/ 鉴别编码的着色剂 颜色—低迁移/减 低干扰 颜色—生物相容 性评估 透明PP PP、ABS、 PC/ABS的抗静电 性能 激光焊接可 快速、可靠地组装 一系列聚合物 半结晶聚合物 的成核剂，例如 HDPE、PP、POM 防止氧气进入的 PET吸氧剂 透明容器（PP、 PE、PETG、COP） 中的紫外光防护 防潮以改善屏障 激光打标的UDI替 代油墨印刷/贴标 PP、ABS、PC和 高温聚合物的颜 色，符合UL认证 为各种聚合物提供多种颜色，能够 为您的工艺提供适用的即用型配方 或母粒 降低不符合现行和拟定法规（如 IVDR）的风险 即用型解决方案/母粒支持针对电器 外壳的UL要求 永久性/非迁移性即用型配方；不受 相对湿度（%）影响的快速静电衰 减时间 不含山梨醇，最大限度地减少潜在 迁移 1.844.4AVIENT www.avient.com 版权所有© 2021埃万特公司。

LIGHTING MANUFACTURER S T R E E T L I G H T A R M • Limit corrosion • Replace metal insert, maintaining strength • Black color • UV resistance, as used for an outdoor application • Electrical isolation • Utilized simulation services from Avient Design to optimize the product’s design for performance and processability • Achieved required ageing test with the support from R&D and ADTS • Replaced the need to use a metal insert, reducing part weight, cost and simplifying the production process OnForce Long Glass Fiber Reinforced Polypropylene Composites KEY REQUIREMENTS WHY AVIENT?

KEY FEATURES • Formulated with 58–80% fiber by weight • Available in rolls of 25 in/63.4 cm wide unidirectional tape, slit widths available up to 2 in/5 cm • Easily recyclable compared to thermoset composites FIBERS FOR POLYSTRAND TAPES • Fiberglass THERMOPLASTIC RESINS • PP • PE • PETG • aPET • PA6 KEY APPLICATIONS • Building & Construction • Automotive • Consumer & Recreation • Oil & Gas PRODUCT BULLETIN 1.844.4AVIENT www.avient.com Copyright © 2024, Avient Corporation.

We wanted to make it easier for our customers to create durable piping systems by developing a plastic flapper valve that could be easily fused onto polyethylene (PE) pipe.

Base Resin ABS PA PBT PC PE PEEK PP PPS Barrel Temperatures °F (°C) Rear Zone 400–475(200–250) 480–540 (248–282) 480–520 (250–270) 480–570 (250–300) 400–445 (200–230) 660–700 (350–475) 400–440 (200–225) 520–600 (270–300) Center Zone 410–480(205–253) 490–550 (254–287) 485–525 (251–273) 500–580 (260–305) 410–455 (207–237) 670–710 (357–385) 410–450 (205–230) 550–610 (285–310) Front Zone 420–490(210–257) 500–560 (260–293) 490–530 (254–276) 515–590 (267–310) 420–465 (213–243) 680–720 (363–400) 420–455 (215–235) 570–620 (300–320) Nozzle 425–500(215–260) 510–570 (265–298) 490–540 (254–282) 530–600 (275–315) 430–475 (220–250) 700–730 (370–395) 430–460 (220–240) 610–620 (320–325) Melt Temperature 425–515(215–270) 510–570 (265–298) 490–540 (254–282) 530–615 (275–325) 430–495 (220–260) 700–725 (370–385) 430–475 (220–250) 610–635 (320–335) Mold Temperature 140–200(60–90) 150–300 (65–148) 140–280 (60–137) 160–240 (70–115) 80–140 (25–60) 300–400 (150–200) 80–140 (25–60) 190–300 (90–150) Drying Parameters 190 (90) 2–4 Hours 0.01%–0.15% 180 (82) 4–5 Hours 0.10%–0.20% 275 (135) 3–4 Hours 0.02%–0.04% 250 (125) 3–4 Hours 0.02% 160 (70) 2 Hours 300 (150) 3–4 Hours 0.10% 160 (70) 2 Hours 280 (135) 2–3 Hours 0.01%–0.20% Nozzle Type General Purpose Nylon or Reverse Taper General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose Injection Velocity1 2–5 in/sec; 50–127 mm/sec Injection Pressure Medium to high (may range from 1,000–4,000 psi; 7-28 Mpa) Back Pressure 50–100 psi; 0.3–0.7 Mpa Screw Speed 25–75 RPM Cushion 0.125–0.250 in; 3–6 mm Screw Compression Ratio2 2.0:1–2.5:1 Processing Guide 3 Base Resin ABS PA PBT PC PE PEEK PP PPS Barrel Temperatures °F (°C) Rear Zone 400–475(200–250) 480–540 (248–282) 480–520 (250–270) 480–570 (250–300) 400–445 (200–230) 660–700 (350–475) 400–440 (200–225) 520–600 (270–300) Center Zone 410–480(205–253) 490–550 (254–287) 485–525 (251–273) 500–580 (260–305) 410–455 (207–237) 670–710 (357–385) 410–450 (205–230) 550–610 (285–310) Front Zone 420–490(210–257) 500–560 (260–293) 490–530 (254–276) 515–590 (267–310) 420–465 (213–243) 680–720 (363–400) 420–455 (215–235) 570–620 (300–320) Nozzle 425–500(215–260) 510–570 (265–298) 490–540 (254–282) 530–600 (275–315) 430–475 (220–250) 700–730 (370–395) 430–460 (220–240) 610–620 (320–325) Melt Temperature 425–515(215–270) 510–570 (265–298) 490–540 (254–282) 530–615 (275–325) 430–495 (220–260) 700–725 (370–385) 430–475 (220–250) 610–635 (320–335) Mold Temperature 140–200(60–90) 150–300 (65–148) 140–280 (60–137) 160–240 (70–115) 80–140 (25–60) 300–400 (150–200) 80–140 (25–60) 190–300 (90–150) Drying Parameters 190 (90) 2–4 Hours 0.01%–0.15% 180 (82) 4–5 Hours 0.10%–0.20% 275 (135) 3–4 Hours 0.02%–0.04% 250 (125) 3–4 Hours 0.02% 160 (70) 2 Hours 300 (150) 3–4 Hours 0.10% 160 (70) 2 Hours 280 (135) 2–3 Hours 0.01%–0.20% Nozzle Type General Purpose Nylon or Reverse Taper General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose Injection Velocity1 2–5 in/sec; 50–127 mm/sec Injection Pressure Medium to high (may range from 1,000–4,000 psi; 7-28 Mpa) Back Pressure 50–100 psi; 0.3–0.7 Mpa Screw Speed 25–75 RPM Cushion 0.125–0.250 in; 3–6 mm Screw Compression Ratio2 2.0:1–2.5:1 Comments 1. PC Compounds: 0.001"–0.002" depth and 0.250" width PC/PSU Compounds: 0.002"–0.003" depth and 0.250" width PES Compounds: 0.003"–0.004” depth and 0.250" width PEI Compounds: 0.001"–0.003” depth and 0.250" width PP Compounds: 0.001"–0.002” depth and 0.250" width ABS Compounds: 0.0015"–0.0025” depth and 0.250" width PEEK Compounds: 0.002"–0.004” depth and 0.250" width Nylon Compounds: 0.002" min. depth and 0.250" width Increase vent depth to 1.0mm (0.040") at 4.0mm (0.250") away from the cavity and vent to atmosphere.

Available in natural and black grades, this Edgetek PKE GF series can be colored at the press.

Available in natural and black grades, LubriOne PKE grades can be colored at the press.

X X X Filler Reduces cost X X X Platinum Flame retardant X X X Extra All peroxides including DBPH catalyst X X X Heat Stabilizer Allows for higher heat in longer periods X X Carbon Black Smoke suppressant X Flame retardant grades may be blended to achieve desired results.