This literature shall NOT operate as permission, recommendation, or inducement to practice any patented invention without permission of the patent owner. 1.844.4AVIENT www.avient.com TEST STANDARD UNIT SYNCURE™ XLPE S1054A ROHS NATURAL Specific Gravity ASTM D1505 – 0.919 Melt Flow Index, 190°C/2.16kg ASTM D1238 g/10min 1.045 Tensile Strength at Break ASTM D638 psi 2500 Tensile Elongation at Break ASTM D638 % 450 Delta Torque Internal g-m 2154 Moisture Content ASTM D2974 % 0.0004 Gel Content ASTM D2765 % 73 Hot Creep Elongation UL 2556 % 49 Hot Deformation UL 2556 % 6 TECHNICAL PROPERTIES *Gel Content, Hot Creep Elongation and Hot Deformation measured on 95 phr S1054A / 5 phr S100B system, and cured by autoclave for 9 hours

TEMPERATURE DISTRIBUTION DIAGRAM • Test Method: FTTS-FA-010-2007 4.2 • Equipment: Thermovision • Heat Source: 500W Halogen Lamp • Heat Distance: 100 cm Surface temperature before exposure: 20.22°C Surface temperature after 10 min exposure: 33.85°C Temperature change: +13.6°C Added Cesa Fiber Additives for heat preservation TEST METHOD STANDARD REQUEST TEST RESULT GB/T30127 Far infrared radiation properties Far infrared emissivity ≥0.88 (5-14um) (Test temperature: 34°C) 0.9 Far infrared radiation temperature rise ≥ 1.4°C 9°C GB/T 18319-2019 Thermal retention with accumulated by infrared ray Maximum temperature rise ≥ 6°C 8.9°C Mean temperature rise ≥ 4.4°C (20 minutes) 5.6°C FTTS-FA-010 Infrared radiation properties & thermal retention temperature rise Average emissivity ≥ 0.8 (2-22um) (Test temperature: 25°C) 0.8 Specified heating ΔT ≥ 0.5°C (relative to the standard) +5.34°C (ΔT) GB/T 11048-2008 Method A Thermal transmittance Unit: clo Naked body: 0 Underwear: 0.04 T-shirt: 0.09 Thick sweater: 0.35 Winter coat: 0.7 All the data above are the reference value 0.625 Human Physiological Experiment Blood flow volume +12.9% Blood flow velocity +13.6% Blood oxygenation(%SpO2) +1.7% www.avient.com Copyright © 2023, Avient Corporation.

Buyer will not alter, add or modify any labeling applied to Product which would alter or affect PolyOne’s obligations or liability for health, safety, or environmental warnings, regulatory-required warnings, express or implied warranties, or product liability. 6.

Santiago, 3 Junio 2021 C ó d ig o d e V e ri fic a ci ó n : 0 1 2 -2 1 0 6 -0 3 0 9 -1 1 4 2 012-2106-0309-1142 Documento incorpora Firma Electronica Avanzada Código de Verificación: cec_1c0abd-0 pagina 2 de 2 EDUARDO JAVIER DIEZ MORELLO 2021-06-03T10:28:54-0600 Santiago Firma Electrónica Notario 2021-06-04T10:37:47-0400

29/6/2021 Formulario de Impresión de Constancia de Inscripción https://seti.afip.gob.ar/padron-puc-constancia-internet/ConsultaConstanciaAction.do 1/1 ADMINISTRACION FEDERAL DE INGRESOS PUBLICOS CONSTANCIA DE INSCRIPCION AVIENT ARGENTINA S.A.

These materials outperform nylon 6 and flexible PVC with better flexibility, lower moisture absorption, better insulation properties, and they are RoHS compliant.

Toluca, Mexico 6. Elyria, Ohio 6. Elyria, Ohio 6.

Base Resin PC PC/PSU PES PEI PP ABS PEEK PA Barrel Temperatures* °F (°C) Rear Zone 530–560 (277–293) 550–575 (288–302) 660–700 (349–371) 675–725 (357–385) 390–420 (199–216) 425–460 (219–238) 680–730 (360–388) 430–500 (221–260) Center Zone 515–560 (269–288) 540–565 (282–296) 650–690 (343–366) 655–710 (352–377) 380–405 (193–207) 415–450 (213–232) 670–710 (354–377) 420–490 (216–254) Front Zone 510–525 (266–274) 530–555 (277–291) 640–680 (338–360) 655–700 (346–371) 370–395 (188–202) 405–440 (207–227) 650–690 (343–366) 410–480 (210–249) Nozzle 520–535 (271–280) 540–565 (282–296) 650–690 (343–366) 665–710 (352–377) 380–400 (193–204) 415–450 (213–232) 660–700 (349–371) 420–490 (216–254) Melt Temperature 525–560 (274–293) 530–580 (277–304) 650–700 (343–371) 660–730 (349–388) 375–395 (191–202) 410–460 (210–238) 650–730 (343–388) 420–500 (216–260) Mold Temperature 175–250 (80–121) 160–220 (71–104) 280–350 (138–177) 275–350 (135–177) 100–135 (38–57) 150–180 (66–82) 300–425 (149–219) 160–230 (71–110) Pack & Hold Pressure 50%–75% of Injection Pressure Injection Velocity in/s 0.5–2.0 Back Pressure psi 50 Screw Speed rpm 40–70 40–70 40–70 40–70 40–70 40–70 40–70 40–70** Drying Parameters °F (°C) 6 hrs @ 250 (121) 4 hrs @ 250 (121) 4 hrs @ 275 (135) 4 hrs @ 250 (121) 3 hrs @ 300 (150) 2 hrs @ 200 (93) 3 hrs @ 275 (135) 4 hrs @ 180 (82) Cushion in 0.125–0.250 Screw Compression Ratio 2.0:1–2.5:1 2.0:1–2.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 Nozzle Type General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose Reverse Taper Clamp Pressure 5–6 Tons/in2 * A reverse temperature profile is important to obtain optimum conductive properties.

Level 5 7.62mm rifle lead core full metal copper jacket, military ball 2750 ft/sec 838 m/sec 1 Level 6 Level II 9mm full metal jacket with lead core 1400 ft/sec 427 m/sec 5 Level 7 5.56mm rifle full metal copper jacket with lead core 3080 ft/sec 939 m/sec 5 Level 8 Level III 7.62mm rifle lead core full metal copper jacket, military ball 2750 ft/sec 838 m/sec 5 Width Length Thickness Color LEVEL 1 GlasArmor Panels 36 in/91 cm 96 in/244 cm 0.256 in/6.5 mm Natural 36 in/91 cm 120 in/305 cm 48 in/122 cm 96 in/244 cm 48 in/122 cm 108 in/274 cm 48 in/122 cm 120 in/305 cm LEVEL 2 GlasArmor Panels 36 in/91 cm 96 in/244 cm 0.384 in/9.8 mm Natural 36 in/91 cm 120 in/305 cm 48 in/122 cm 96 in/244 cm 48 in/122 cm 108 in/274 cm 48 in/122 cm 120 in/305 cm LEVEL 3 GlasArmor Panels 36 in/91 cm 96 in/244 cm 0.500 in/12.7 mm Natural 36 in/91 cm 120 in/305 cm Natural 48 in/122 cm 96 in/244 cm Natural, Grey, White, Tan 48 in/122 cm 108 in/274 cm Natural, Grey 48 in/122 cm 120 in/305 cm Natural, Grey, White ThermoBallistic Panels 24 in/61 cm 96 in/244 cm 0.44 in/11.2 mm White, Grey, Blue 24 in/61 cm 144 in/366 cm 48 in/122 cm 96 in/244 cm 48 in/122 cm 144 in/366 cm BALLISTIC PANEL SELECTION GUIDE Customized panel sizes and colors available. Position these batten strips to cover the seam and attach to both panels using appropriate wallboard screws (see diagram). 6.

Wschdnia 6, 99-300, Kutno Poland Logistic 2/2 https://e-cer.bureauveritas.com/FMSNR3ILR1QPBBMGXNKFUDB2LWB28AYDXJNZADBZ8WDH3QYML73QK0B7L7V6CZQPGPGDYLG2UVXWEPJVT4Q0E4Z0DOKSEXCP0BNO7K2WUHCQB2Q9ORVVTV4F9DTN2UI35L https://e-cer.bureauveritas.com/FMSNR3ILR1QPBBMGXNKFUDB2LWB28AYDXJNZADBZ8WDH3QYML73QK0B7L7V6CZQPGPGDYLG2UVXWEPJVT4Q0E4Z0DOKSEXCP0BNO7K2WUHCQB2Q9ORVVTV4F9DTN2UI35L https://e-cer.bureauveritas.com/FMSNR3ILR1QPBBMGXNKFUDB2LWB28AYDXJNZADBZ8WDH3QYML73QK0B7L7V6CZQPGPGDYLG2UVXWEPJVT4Q0E4Z0DOKSEXCP0BNO7K2WUHCQB2Q9ORVVTV4F9DTN2UI35L https://e-cer.bureauveritas.com/FMSNR3ILR1QPBBMGXNKFUDB2LWB28AYDXJNZADBZ8WDH3QYML73QK0B7L7V6CZQPGPGDYLG2UVXWEPJVT4Q0E4Z0DOKSEXCP0BNO7K2WUHCQB2Q9ORVVTV4F9DTN2UI35L https://e-cer.bureauveritas.com/FMSNR3ILR1QPBBMGXNKFUDB2LWB28AYDXJNZADBZ8WDH3QYML73QK0B7L7V6CZQPGPGDYLG2UVXWEPJVT4Q0E4Z0DOKSEXCP0BNO7K2WUHCQB2Q9ORVVTV4F9DTN2UI35L https://e-cer.bureauveritas.com/FMSNR3ILR1QPBBMGXNKFUDB2LWB28AYDXJNZADBZ8WDH3QYML73QK0B7L7V6CZQPGPGDYLG2UVXWEPJVT4Q0E4Z0DOKSEXCP0BNO7K2WUHCQB2Q9ORVVTV4F9DTN2UI35L https://e-cer.bureauveritas.com/FMSNR3ILR1QPBBMGXNKFUDB2LWB28AYDXJNZADBZ8WDH3QYML73QK0B7L7V6CZQPGPGDYLG2UVXWEPJVT4Q0E4Z0DOKSEXCP0BNO7K2WUHCQB2Q9ORVVTV4F9DTN2UI35L