关键性能 加工信息 1 1 物理性能 标称值 标称值 单位 测试法 1.00 ASTM D792 20 g/10 min ASTM D1238 抗拉强度 密度/比重 熔指 (MFR) (230°C/2.16kg) 15.0 MPa ASTM D638 1400 MPa ASTM D790 35.0 MPa ASTM D790 150 J/m ASTM D256 < 100000 ohms/sq ASTM D257 80 to 90 °C 4.0 to 6.0 hr 220 to 250 °C 30 to 80 °C 机械 弯曲模量 弯曲强度 悬臂梁缺口冲击强度（注塑样条） 冲击 电气 表面电阻率 干燥温度 注塑 干燥时间 加工（熔化）温度 模具温度 主要性能：不能被解释为技术指标 单位 Trilliant HC™ 方案如何协助攻克严苛的性能和工艺挑战 www.avient.com 版权所有©2022 埃万特公司。

Injection Molding Parameters Base Resin PA6 PA6 IM/ST PA6 GF PA6 GMF PA66 IM/ST PA66 GF Barrel Temperatures °F (°C) Rear Zone 450–490 (232–254) 440–490 (226–254) 490–510 (254–265) 480–500 (249–260) Center Zone 460–500 (238–260) 450–500 (232–260) 500–520 (260–271) 490–510 (254–265) 520–540 (271–282) Front Zone 470–510 460–510 (237–265) 500–520 (260–271) Nozzle 480–520 (249–271) 470–510 515–530 (268–276) 530–560 (276–293) 540–560 (282–293) Melt Temperature °F (°C) 480–520 (249–271) 470–510 515–530 (268–276) 540–560 (282–293) Mold Temperature °F (°C) 120–180 (49–82) 120–180 (49–82) 120–200 (49–93) 120–200 (49–93) 140–220 (60–104) 140–220 (60–104) Pack and Hold Pressure 50–80% of Injection Pressure Injection Velocity 1.0–4.0 in/sec Back Pressure 25–100 psi Screw Speed 35–80 rpm Drying Parameters 4 hours @ 180°F (82°C) Moisture Allowable 0.1–0.2% Cushion 0.250 in Screw Compression Ratio 2.0:1–2.5:1 Nozzle Type Reverse Taper Clamp Pressure 3–5 tons/in2 Processing Guide 3 Start Up & Shut Down Recommendations Purge Compound Polypropylene Recycling Recycling prime grades up to 20% is permissible and recycling PIR or PCR grades up to 10% is permissible.

PDI) on extruded profiles 2 ASTM D-638 3 ASTM 256 4 ASTM D-648 66 psi, unannealed, 0.125" 5 Savings depends on profile size and production volume Acrylite is a registered trademark of Evonik Performance Materials Lens Performance Resilience™ LS Frost PVC Acrylite® Satinice Frost PMMA Light Transmission1 at 0.060" (1.5mm) 83% Low Diffusion 78% Medium Diffusion 75% High Diffusion 81% Low Diffusion Diffusion Half Power Angle (DLD) 26° Low Diffusion 41° Medium Diffusion 58° High Diffusion 26° Low Diffusion Tensile Strength2 Tensile Modulus2 Tensile Elongation (break)2 7,360 psi 400,000 psi 20% 7,330 psi 330,000 psi 43% Flammability (UL 94) V-0 @ 1.5mm 5VA @ 2.0mm HB @ 1.6mm Notched Izod Impact (73°F)3 2.3 ft-lb/in 0.6 ft-lb/in Heat Deflection Temperature4 157°F/69°C 182°F/83°C UV Stability Good Excellent Chemical Resistance Excellent Good Typical Lens Profile Cost 10–15% Savings5 Baseline 1.866.POLYONE www.polyone.com Copyright © 2018, PolyOne Corporation.

Peel, PLI 12 19 23 20 19 reSound OM 5510 for PP reSound OM 5510-60N Room Temperature 70C Bio-derived Content (%) 50% 50% 50% 50% 50% 50% 50% Hardness, Shore A 60 60 60 60 60 60 60 Specific Gravity 0.89 0.89 0.89 0.89 0.89 0.89 0.90 50% Modulus, PSI 247 241 244 251 234 244 240 100% Modulus, PSI 343 333 338 339 321 331 326 Tensile Strength, PSI 625 621 647 610 633 662 642 Elongation, % 306 314 309 313 312 315 315 Tear Strength, PLI 109 108 113 113 111 117 115 reSound OM 5520-55N Room Temperature 70C Bio-derived Content (%) 49% 49% 49% 49% 49% 49% 49% Hardness, Shore A 54 54 55 55 54 55 56 Specific Gravity 0.95 0.95 0.96 0.96 0.95 0.96 0.96 50% Modulus, PSI 258 256 256 265 266 271 257 100% Modulus, PSI 353 355 357 362 373 379 367 Tensile strength, PSI 637 615 637 669 651 674 642 Elongation, % 319 315 319 333 313 319 315 Tear Strength, PLI 146 136 133 142 137 138 141 reSound OM 5510-45N Room Temperature 70C Bio-derived Content (%) 40% 40% 40% 40% 40% 40% 40% Hardness, Shore A 45 46 47 46 46 45 45 Specific Gravity 0.88 0.89 0.89 0.89 0.89 0.89 0.90 50% Modulus, PSI 153 158 154 162 137 136 133 100% Modulus, PSI 251 259 259 261 226 222 218 Tensile Strength, PSI 438 481 451 495 417 470 486 Elongation, % 215 240 211 243 204 227 238 Tear Strength, PLI 84 81 87 82 83 85 84 AGING – PROPERTY RETENTION • Tested at room temperature and 70° C for comparison • Hardness, tensile strength elongation and modulus showed great retention Overmolding onto PP Overmolding onto ABS RHEOLOGY Suitable for injection molding and overmolding 1.0 10 100 1000 10000 100000 10.0 100.0 1000.0 reSound OM 5510-30N reSound OM 5510-45N reSound OM 5510-60N reSound OM 5510-70N Shear Rate, 1/s Ca pi lla ry V is co si ty , P a* s 1.0 10 100 1000 10000 100000 10.0 100.0 1000.0 reSound OM 5520-55N Shear Rate, 1/s Ca pi lla ry V is co si ty , P a* s Capillary viscosity at 200°C Capillary viscosity at 200°C reSound OM 5510 for PP reSound OM 5520 for ABS www.avient.com Copyright © 2020, Avient Corporation.

ACTIVE INGREDIENTS RESISTANCE RATING Clorox® Disinfecting Wipes 5813-79 Quaternary ammonium +++++ +++++ +++++ ++ +++ ++++ Formula 409® Heavy Duty Degreaser N/A Lauramine oxide, ethanolamine +++++ +++++ +++++ + ++ +++ Lysol® All-Purpose Cleaner 777-66 Quaternary ammonium +++++ +++++ +++++ + + ++ $$$ $$$ $$$$ $ $$$ $ MATERIAL COMPARISON WITH COMMON CONSUMER DISINFECTANTS P AB S P PE T P PB T E 90 0 CR E 90 0 H I C R E 92 0 C RCRITERIA FOR RESISTANCE RATING + strength and elongation at yield retention between 90-110% + strength and elongation at yield retention between 75-125% + no statistically significant reduction in elongation at break (p < 0.05) + visual observation score of 4 or better (minor/no crazing, no cracks) + samples survived disinfectant exposure in strain jig Lysol® is a trademark of Reckitt Benckiser LLC Formula 409® is a trademark of The Clorox Company Clorox® is a trademark of The Clorox Company An independent, A2LA-accredited lab tested the following polymers with various disinfectants to help customers choose the material suitable for their specific application requirements.

These robust materials also incorporate heat stabilization to maintain tensile strength and tensile elongation properties for long- term thermal aging up to 120°C. Edgetek™ ET9700-0031 HI HS NAT Edgetek™ ET9700-0033 20GF HI HS NAT Edgetek™ ET9700-0032 35GF HI HS NAT Description Unfilled GF 20% GF 35% Color Natural & Black Natural & Black Natural & Black Notched Impact (kJ/m2) 19.0 13.8 13 Un-Notched Impact (kJ/m2) No Break 73 87 HDT, 1.83 MPa (°C) 112 182 258 Tensile Strength, yield (MPa) 60 106 183 Tensile Elongation, yield (%) 6.0 3.5 2.2 Flexural Modulus (MPa) 2235 5288 9058 Flexural Strength (MPa) 96 170 264 Heat Stabilization Yes Yes Yes

KEY CHARACTERISTICS • DBDPE-free • Excellent flame performance • Resistance to heat, oil, creep, and abrasion • Temperature rating up to 90°C • High extrusion speeds • UL 44 compliant Copyright © 2023, Avient Corporation. This literature shall NOT operate as permission, recommendation, or inducement to practice any patented invention without permission of the patent owner. 1.844.4AVIENT www.avient.com System Syncure XLPE S200FH Syncure XLPE S200FV Applications Building Wire, Tray Cable, Service Entrance Building Wire, Tray Cable, Service Entrance Specification UL 44 UL 44 Wire Type RHW-2, RHW, RHH, XHHW-2, XHH, XHHW, SIS RHW, RHH, RHW-2 Components 78% S1054A 22% SC5400-0002 RoHS MB ALT FR 50% S1054A 50% SC5400-0003 RoHS MB ALT FR Features Horizontal Flame, DBDPE-free VW-1, DBDPE-free General Properties Specific Gravity (g/cm3) 1.01 1.31 Hardness Shore D, 10sec 47 48 Gel % 68 70 Tensile Properties Tensile Strength (psi) 2800 3200 Elongation % 400 470 Tensile Retention % 95 100 Elongation Retention % 90 93 Electrical Dielectric Strength (V/mil) 1000 1200 Dielectric Constant 2.31 2.61 Dissipation Factor % 0.0012 0.0043 Thermal Temperature Rating °C 90 90 Heat Deformation % 10 5 TECHNICAL PROPERTIES

KEY CHARACTERISTICS • Resistant to heat, oil, creep and abrasion • Flame performance • Low temperature performance • Temperature ratings up to 125°C • High extrusion speeds, ambient curing properties and low capital investment • Conforms to UL-44, UL-4703 and CSA 22.2 requirements MARKETS AND APPLICATIONS Syncure XLPE formulations provide economical solutions for multiple end-use commercial and residential applications. This literature shall NOT operate as permission, recommendation, or inducement to practice any patented invention without permission of the patent owner. 1.844.4AVIENT www.avient.com TEST STANDARD UNIT SYNCURE™ XLPE S1054A ROHS NATURAL Specific Gravity ASTM D1505 – 0.919 Melt Flow Index, 190°C/2.16kg ASTM D1238 g/10min 1.045 Tensile Strength at Break ASTM D638 psi 2500 Tensile Elongation at Break ASTM D638 % 450 Delta Torque Internal g-m 2154 Moisture Content ASTM D2974 % 0.0004 Gel Content ASTM D2765 % 73 Hot Creep Elongation UL 2556 % 49 Hot Deformation UL 2556 % 6 TECHNICAL PROPERTIES *Gel Content, Hot Creep Elongation and Hot Deformation measured on 95 phr S1054A / 5 phr S100B system, and cured by autoclave for 9 hours

They are developed to achieve GWFI 960°C ratings with a maximum of 30 seconds post combustion time. APPLICATIONS • Electrical and electronic enclosures and housings • Junction boxes • Switches, connectors and plugs • Power outlet components • Covers and windows in E&E parts BENEFITS • Formulated without PTFE which is typically used as anti-drip agent • Non-halogen in accordance with the IEC 61249-2-21 standard • Achieves GWFI 960°C temperature (with max. 30 sec post combustion time) according to IEC 60695-2-12 • Can be combined with colors and other additives for added convenience and increased performance PRODUCT OVERVIEW Copyright © 2023, Avient Corporation.

In trials with various washing machines and modes, they show excellent peel strength and resistance to discoloration, fading, or hazing at water temperatures up to 60°C. KEY CHARACTERISTICS • High-wearing comfort and elastic recovery • Strong and seamless adhesion to polyester and nylon fabrics • Passed OEKO-TEX 100-2 testing • Excellent washability at up to 60°C • Non-toxic formulations with low volatile organic compounds (VOC) and without added plasticizers • Attractive alternative to conventional TPU adhesive film and glue MARKETS & APPLICATIONS Versaflex TF Adhesive TPE solutions have been custom engineered for: • Elastic strips in underwear • Seam tapes in sports and fitness apparel PRODUCT BULLETIN 1.844.4AVIENT www.avient.com Copyright © 2024, Avient Corporation.